Survey Of Potential-Induced Degradation In Thin-Film Modules

Keywords

accelerated lifetime testing; CdTe; copper indium gallium (di)selenide; current-induced degradation; potential-induced degradation

Abstract

Two CdTe and two copper indium gallium (di)selenide (CIGS)-type modules were tested for potential-induced degradation (PID) with positive and negative 1000 V biases applied to the active cell circuit in an 85°C, 85% relative humidity environmental chamber. Various degradation mechanisms could be seen with signatures such as shunting, transparent conductive oxide (TCO) corrosion, charge carrier lifetime reduction, and dead active layer at edges along with resulting cell mismatch. All modules tested exhibited degradation by system voltage stress in chamber, but only one module type has degraded in parallel field tests. I-V curve data indicated that one CdTe-type module sequentially exhibited shunting followed by a recovery and then series resistance losses. This module type showed TCO delamination from the glass in the environmental chamber tests and also exhibited power degradation within 5 weeks in field tests. Relative rates of Coulomb transfer from the voltage-biased active cell circuit to ground are compared for the modules in chamber tests to those placed outdoors under system voltage stress to extrapolate the anticipated time to failure in the field. This analysis correctly indicated which module type failed in the field first.

Publication Date

1-1-2015

Publication Title

Journal of Photonics for Energy

Volume

5

Issue

1

Document Type

Editorial Material

Personal Identifier

scopus

DOI Link

https://doi.org/10.1117/1.JPE.5.053083

Socpus ID

84952685566 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/84952685566

This document is currently not available here.

Share

COinS