Effect Of Drilling Allowance On Tbc Delamination, Spatter And Re-Melted Cracks Characteristics In Laser Drilling Of Tbc Coated Superalloys

Keywords

Drilling allowance; Laser drilling; Re-melted cracks; Spatter; TBC delamination; Thermal barrier coating

Abstract

Laser drilling of inclined holes on Ni-based superalloys coated with thermal barrier coatings (TBC) was studied using numerical simulation and experiments. Two types of drilling, three steps-laser drilling (TSLD) method and the one step laser drilling (OSLD), were employed for making comparison. The simulation results demonstrate that relatively strong vortex effect of assist gas at hole entrance and the drilling allowance of the substrate hole can deflect the trajectories of melt flow from leading edge TBC wall. This phenomenon may isolate leading edge of the hole from the ejecting molten material. Thus, shearing stress effect was prevented. The characteristics of TBC delamination, spatter at the TBC leading edge and re-melted cracks along the TBC trailing edge are investigated by comparing the characteristics of the melt flow obtained via simulation and experiment. The combined results suggest that the TBC/substrate multilayer can avoid these defects applying the TSLD technology.

Publication Date

7-1-2016

Publication Title

International Journal of Machine Tools and Manufacture

Volume

106

Number of Pages

1-10

Document Type

Article

Personal Identifier

scopus

DOI Link

https://doi.org/10.1016/j.ijmachtools.2016.03.008

Socpus ID

84962911187 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/84962911187

This document is currently not available here.

Share

COinS