Liquefaction Of Lignin In Hot-Compressed Water To Phenolic Feedstock For The Synthesis Of Phenol-Formaldehyde Resins

Keywords

Adhension; Chemical analysis; Cure; Mechanical testing; Resins

Abstract

The corn stalk lignin was liquefied in hot-compressed water without any other additives to obtain the degraded liquids (DL) with liquefaction yields of 45.9–61.4 wt%, under 3.4 MPa and 260 °C. The degradation liquids, mainly composed of small molecular phenols as high as 84.6 wt%, were put to use as substitutes for phenol to modify phenol-formaldehyde resin. The degradation liquids modified phenol-formaldehyde resins (DLPFs) possessed the highest adhesive strength (1.32 ± 0.10 MPa) than the lignin-phenol-formaldehyde resin (LPF, 0.72 ± 0.20 MPa) and typical phenol-formaldehyde resin (PF, 0.77 ± 0.26 MPa). The free formaldehyde contents of the DLPFs were all lower than the requirement of the corresponding standard (≤0.3 wt%), even when 60% of phenol was replaced by DL (0.232 wt%). The curing behavior analysis showed that the introducing of DL notably decreased the curing activation energy. The results demonstrated that the DLs were very suitable substitution for phenol in preparation of DLPFs. The adhesive strengths of DLPFs were considerably improved compared with typical PF. The thermal curing kinetic analysis revealed that the values of activation energy were decreased obviously with the introduction of DL.

Publication Date

3-1-2017

Publication Title

Composites Part B: Engineering

Volume

112

Number of Pages

8-14

Document Type

Article

Personal Identifier

scopus

DOI Link

https://doi.org/10.1016/j.compositesb.2016.10.094

Socpus ID

85009723343 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/85009723343

This document is currently not available here.

Share

COinS