Interdiffusion And Reactions Between U-Mo And Zr At 650°C As A Function Of Time

Abstract

Development of monolithic U-Mo alloy fuel (typically U-10 wt.%Mo) for the Reduced Enrichment for Research and Test Reactors (RERTR) program entails a use of Zr diffusion barrier to eliminate the interdiffusion-reactions between the fuel alloy and Al-alloy cladding. The application of Zr barrier to the U-Mo fuel system requires a co-rolling process that utilizes a soaking temperature of 650°C, which represents the highest temperature the fuel system is exposed to during both fuel manufacturing and reactor application. Therefore, in this study, development of phase constituents, microstructure and diffusion kinetics of U-10 wt.%Mo and Zr was examined using solid-to-solid diffusion couples annealed at 650°C for 240, 480 and 720 h. Phase constituents and microstructural development were analyzed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Concentration profiles were mapped as diffusion paths on the isothermal ternary phase diagram. Within the diffusion zone, single-phase layers of β-Zr and β-U were observed along with a discontinuous layer of Mo2Zr between the β-Zr and β-U layers. In the vicinity of Mo2Zr phase, islands of α-Zr phases were also found. In addition, acicular α-Zr and U6Zr3Mo phases were observed within the γ-U(Mo) terminal alloy. Growth rate of the interdiffusion-reaction zone was determined to be 7.75 (± 5.84) × 10-16 m2/s at 650°C, however with an assumption of a certain incubation period.

Publication Date

1-1-2015

Publication Title

Journal of Nuclear Materials

Volume

456

Number of Pages

351-358

Document Type

Article

Personal Identifier

scopus

DOI Link

https://doi.org/10.1016/j.jnucmat.2014.09.040

Socpus ID

84908538061 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/84908538061

This document is currently not available here.

Share

COinS