Quantification Of Nitrogen Impurity And Estimated Orowan Strengthening Through Secondary Ion Mass Spectroscopy In Aluminum Cryomilled For Extended Durations

Keywords

Aluminum alloy; Cryomilling; Nitrogen; Orowan strengthening; Secondary ion mass spectrometry

Abstract

The strength of aluminum alloys and composites processed through powder metallurgy can be improved through the addition of nano-scale dispersoids introduced during the cryomilling process. Quantification of Orowan strengthening from these dispersoids requires a reliable measurement of the impurity concentration. Secondary ion mass spectrometry (SIMS) was used to quantify the nitrogen impurity concentration using a 14N ion implanted standard. An analytical approach is devised to determine the nitrogen concentration of an aluminum alloy and composite based on SIMS measurements. Results are compared to the measurements carried out by gas fusion analysis. An increase in nitrogen concentration was observed with an increase in cryomilling time up to 72h. The nitrogen concentration varied from 1.64±0.17at% (0.80±0.08wt%) to 19.12±1.10at% (13.17±0.71wt%) for the 8h and 72h cryomilled nanocrystalline AA5083, respectively. Assuming that all nitrogen reacts to form dispersoids, the nitrogen concentration determined was used to calculate the volume and weight fractions of dispersoids, which in turn was used to estimate the strengthening contribution via Orowan strengthening. Orowan strengthening was calculated using dispersoids of 3, 9 and 15nm. The range of Orowan strengthening contribution was estimated, in MPa, to be from 7.69±0.78 to 3.03±0.31 for the 8h nanocrystalline AA5083 sample, and 154.97±10.29 to 61.09±4.06 for the 72h nanocrystalline AA5083 sample.

Publication Date

11-11-2015

Publication Title

Materials Science and Engineering A

Volume

648

Number of Pages

412-417

Document Type

Article

Personal Identifier

scopus

DOI Link

https://doi.org/10.1016/j.msea.2015.09.007

Socpus ID

84942852096 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/84942852096

This document is currently not available here.

Share

COinS