Comparison Of Commercially Available And Synthesized Titania Nano-Additives In Composite Htpb/Ap Propellant

Keywords

AP; HTPB; Nano-additives; Titania

Abstract

This study presents a comparison of commercially available titania nano-particles produced using electric wire explosion with nano-particles manufactured by the authors using a sol-gel synthesis process. For the present study, 20-nm titania was purchased off-the-shelf. It was determined to be rough spheres of 20 nm forming large, micron-sized agglomerates, whereas particles synthesized using the sol-gel process were found to be fundamentally 10 nm but with sub-micron agglomerations thereof. The nano-titania was added to 80% AP monomodal propellants at 0.3% and 1.0% by mass. Additional, 85% bimodal-AP mixtures were made, comparing commercial titania to the laboratory-synthesized particles at 1.0% by mass. Another set of samples compared a method of pre-mixing the synthesized additives directly into the binder material at 0.3% by mass of laboratory titania; two additional pre-mixed titania batches at 0.5% by mass were doped with either Fe or Cu into the nanocrystals. All propellants were tested up to 13.8 MPa at 3.8 MPa increments. Dry powder laboratory additives show a 60-to-100% increase in burning rate over the baseline samples with no catalyst and a 20-to-30% increase over the commercial nano-particles. Pre-mixed additives were found to produce similar burning rate increases but with lower concentrations required. This latest generation of particle synthesis techniques was further demonstrated in this study to have great potential for future propellant catalyst development.

Publication Date

2-1-2017

Publication Title

Propellants, Explosives, Pyrotechnics

Volume

42

Issue

2

Number of Pages

158-166

Document Type

Article

Personal Identifier

scopus

DOI Link

https://doi.org/10.1002/prep.201600022

Socpus ID

85007228186 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/85007228186

This document is currently not available here.

Share

COinS