In Situ Monitoring Of Pb2+ Leaching From The Galvanic Joint Surface In A Prepared Chlorinated Drinking Water

Abstract

A novel method using a micro-ion-selective electrode (micro-ISE) technique was developed for in situ lead monitoring at the water-metal interface of a brass-leaded solder galvanic joint in a prepared chlorinated drinking water environment. The developed lead micro-ISE (100 μm tip diameter) showed excellent performance toward soluble lead (Pb2+) with sensitivity of 22.2 ± 0.5 mV decade-1 and limit of detection (LOD) of 1.22 × 10-6 M (0.25 mg L-1). The response time was less than 10 s with a working pH range of 2.0-7.0. Using the lead micro-ISE, lead concentration microprofiles were measured from the bulk to the metal surface (within 50 μm) over time. Combined with two-dimensional (2D) pH mapping, this work clearly demonstrated that Pb2+ ions build-up across the lead anode surface was substantial, nonuniform, and dependent on local surface pH. A large pH gradient (ΔpH = 6.0) developed across the brass and leaded-tin solder joint coupon. Local pH decreases were observed above the leaded solder to a pH as low as 4.0, indicating it was anodic relative to the brass. The low pH above the leaded solder supported elevated lead levels where even small local pH differences of 0.6 units (ΔpH = 0.6) resulted in about four times higher surface lead concentrations (42.9 vs 11.6 mg L-1) and 5 times higher fluxes (18.5 × 10-6 vs 3.5 × 10-6 mg cm-2 s-1). Continuous surface lead leaching monitoring was also conducted for 16 h.

Publication Date

2-20-2018

Publication Title

Environmental Science and Technology

Volume

52

Issue

4

Number of Pages

2126-2133

Document Type

Article

Personal Identifier

scopus

DOI Link

https://doi.org/10.1021/acs.est.7b05526

Socpus ID

85042315344 (Scopus)

Source API URL

https://api.elsevier.com/content/abstract/scopus_id/85042315344

This document is currently not available here.

Share

COinS