Keywords

phosphate corrosion inhibitor, metal release, drinking water distribution system, lead and copper rule, blended water quality

Abstract

This study evaluated the effects of orthophosphate (OP) inhibitor addition on iron, copper, and lead corrosion on coupons exposed to different blends of groundwater, surface water, and desalinated seawater. The effectiveness of OP inhibitor addition on iron, copper, and lead release was analyzed by statistical comparison between OP treated and untreated pilot distribution systems (PDS). Four different doses of OP inhibitor, ranging from zero (control) to 2 mg/L as P, were investigated and non-linear empirical models were developed to predict iron, copper, and lead release from the water quality and OP doses. Surface characterization evaluations were conducted using X-ray Photoelectron Spectroscopy (XPS) analyses for each iron, galvanized steel, copper, and lead/tin coupon tested. Also, a theoretical thermodynamic model was developed and used to validate the controlling solid phases determined by XPS. A comparison of the effects of phosphate-based corrosion inhibitor addition on iron, copper, and lead release from the PDSs exposed to the different blends was also conducted. Three phosphate-based corrosion inhibitors were employed; blended orthophosphate (BOP), orthophosphate (OP), and zinc orthophosphate (ZOP). Non-linear empirical models were developed to predict iron, copper, and lead release from each PDS treated with different doses of inhibitor ranging from zero (control) to 2 mg/L as P. The predictive models were developed using water quality parameters as well as the inhibitor dose. Using these empirical models, simulation of the water quality of different blends with varying alkalinity and pH were used to compare the inhibitors performance for remaining in compliance for iron, copper and lead release. OP inhibitor addition was found to offer limited improvement of iron release for the OP dosages evaluated for the water blends evaluated compared to pH adjustment alone. Empirical models showed increased total phosphorus, pH, and alkalinity reduced iron release while increased silica, chloride, sulfate, and temperature contributed to iron release. Thermodynamic modeling suggested that FePO4 is the controlling solid that forms on iron and galvanized steel surfaces, regardless of blend, when OP inhibitor is added for corrosion control. While FePO4 does not offer much control of the iron release from the cast iron surfaces, it does offer protection of the galvanized steel surfaces reducing zinc release. OP inhibitor addition was found to reduce copper release for the OP dosages evaluated for the water blends evaluated compared to pH adjustment alone. Empirical models showed increases in total phosphorus, silica, and pH reduced copper release while increased alkalinity and chloride contributed to copper release. Thermodynamic modeling suggested that Cu3(PO4)2·2H2O is the controlling solid that forms on copper surfaces, regardless of blend, when OP inhibitor is added for corrosion control. OP inhibitor addition was found to reduce lead release for the OP dosages evaluated for the water blends evaluated compared to pH adjustment alone. Empirical models showed increased total phosphorus and pH reduced lead release while increased alkalinity, chloride, and temperature contributed to lead release. Thermodynamic modeling suggested that hydroxypyromorphite is the controlling solid that forms on lead surfaces, regardless of blend, when OP inhibitor is added for corrosion control. The comparison of phosphate-based inhibitors found increasing pH to reduce iron, copper, and lead metal release, while increasing alkalinity was shown to reduce iron release but increase copper and lead release. The ZOP inhibitor was not predicted by the empirical models to perform as well as BOP and OP at the low dose of 0.5 mg/L as P for iron control, and the OP inhibitor was not predicted to perform as well as BOP and ZOP at the low dose of 0.5 mg/L as P for lead control. The three inhibitors evaluated performed similarly for copper control. Therefore, BOP inhibitor showed the lowest metal release at the low dose of 0.5 mg/L as P for control of iron, copper, and lead corrosion.

Notes

If this is your thesis or dissertation, and want to learn how to access it or for more information about readership statistics, contact us at STARS@ucf.edu

Graduation Date

2008

Advisor

Duranceau, Steven

Degree

Doctor of Philosophy (Ph.D.)

College

College of Engineering and Computer Science

Department

Civil and Environmental Engineering

Degree Program

Environmental Engineering

Format

application/pdf

Identifier

CFE0002382

URL

http://purl.fcla.edu/fcla/etd/CFE0002382

Language

English

Release Date

December 2008

Length of Campus-only Access

None

Access Status

Doctoral Dissertation (Open Access)

Download

Share

COinS